Influence of annealing under load on magneto-optical properties of iron-based nanocrystalline ribbons

Capa

Citar

Texto integral

Resumo

The results of the influence of load annealing on the magneto-optical properties of soft magnetic nanocrystalline e68.5Cr5Si13.5B9Nb3Cu1 ribbons obtained by rapid quenching from the melt and then annealed at a temperature of 520°C for 2 h without load and using a specific load of 150 MPa are presented. The near-surface magnetic hysteresis loops and simultaneous visualization of the changes of magnetic domain structure were measured using a magneto-optical Kerr magnetometer. The obtained experimental data that annealing underload leads to the formation of induced magnetic anisotropy and affects the magnetic field behavior of the samples.

Sobre autores

A. Kharlamova

Moscow State University

Email: ama-h-m@mail.ru
Faculty of Physics Moscow, Russia

P. Kozhevnikova

Moscow State University

Faculty of Physics Moscow, Russia

T. Kaminskaya

Moscow State University

Faculty of Physics Moscow, Russia

G. Kuriyandskaya

Institute of Natural Sciences and Mathematics, Ural Federal University

Ekaterinburg, Russia

E. Shalygina

Moscow State University

Faculty of Physics Moscow, Russia

Bibliografia

  1. McHenry M., Willard M.A., Laughlin D.E. // Progr. Mater. Sci. 1999. V44. P. 291.
  2. Kuriyandskaya G.V., Lukshina V.A., Larranaga A. et al. // J. Alloys Compounds. 2013. V. 566. P. 31.
  3. Ершов Н.В., Лукшина В.А., Федоров В.Н. и др. // ФТТ. 2013. Т. 55. № 3. С. 460; Ershov N.V., Lukshina V.A., Fedorov V.I. et al. // Phys. Solid State. 2013. V. 55. No. 3. P. 508.
  4. Serikov V.V., Kleinerman N.M., Volkova E.G. et al. // Phys. Metal. Metallogr. 2006. V. 102. P. 268.
  5. Moulin J., Mazaleyrat F., Mendez A., Dufour-Gergam E. // J. Magn. Magn. Mater. 2010. V. 322. P. 1275.
  6. Ершов Н.В., Черненков Ю.П., Лукшина В.А. и др. // ФТТ. 2021. Т. 63. № 7. С. 834; Ershov N.V., Chernenkov Y.P., Fedorov V.I. et al. // Phys. Solid State. 2021. V. 63. No. 7. P. 978.
  7. Vazquez M., Kuriyandskaya G.V., Garcia-Beneytez J.M. et al. // IEEE Trans. Magn. 1999. V. 35. No. 5. P. 3358.
  8. Hofmann B., Krommuller H. // J. Magn. Magn. Mater. 1996. V. 152. No. 91. P. 91.
  9. Ohnuma M., Hono K., Yanai T. et al. // Appl. Phys. Lett. 2003. V. 83. No. 14. P. 2859.
  10. Миронов Д.Я. Основы сканирующей зондовой микроскопии. Нижний Новгород: ИФМ РАН, 2004. 114 с.
  11. Ершов Н.В., Федоров В.Н., Черненков Ю.П. и др. // ФТТ. 2017. Т. 59. № 9. С. 1724; Ershov N.V., Fedorov V.I., Chernenkov Y.P. et al. // Phys. Solid State. 2017. V. 59. No. 9. P. 1748.
  12. Шалыгина Е.Е., Молоканов В.В., Комарова М.А. // ЖЭТФ. 2002. Т. 122. № 3. С. 593; Shalygina E.E., Molokanov V.V., Komarova M.A. // JETP. 2002. V. 95. P. 511.
  13. Kuriyandskaya G.V., Lezama L., Pasyukova A.A. et al. // Materials. 2022. V. 15. P. 4160.
  14. Hubert A., Schäfer R. Magnetic Domains. Berlin: Springer, 1998. P. 686.

Arquivos suplementares

Arquivos suplementares
Ação
1. JATS XML
Baixar

Declaração de direitos autorais © Russian Academy of Sciences, 2025