Comparison of optical properties and radiation stability of Gd2O3 micro- and nanopowders

Мұқаба

Дәйексөз келтіру

Толық мәтін

Ашық рұқсат Ашық рұқсат
Рұқсат жабық Рұқсат берілді
Рұқсат жабық Тек жазылушылар үшін

Аннотация

The results of comparative studies of the phase composition, diffuse reflectance spectra, radiation-induced absorption spectra, and the integral absorption coefficient of solar radiation upon irradiation of micro- and nanopowders of gadolinium oxide are presented. To assess the radiation resistance of optical properties, the samples were placed in a chamber of an installation simulating space conditions, where diffuse reflection spectra were recorded in the range of 0.2–2.5 μm in a vacuum of 2×10–6 Torr before and after each period of electron irradiation (E = 30 keV, Φ = (1 – 3)×1016 cm–2). Micropowders of rare earth elements are used to increase the radiation stability of materials by absorbing free electrons formed in them during irradiation during their transitions from the d- to f-shell. Nanopowders of rare earth elements added to micropowders of various compounds provide an additional mechanism for increasing radiation stability due to the annihilation of primary defects formed during irradiation on nanoparticles. The work obtained a result opposite to these mechanisms - the radiation stability of micropowder is significantly (more than 4 times) higher compared to nanopowder, due to more intense absorption in the ultraviolet region for nanopowder, caused by its own defects. The paper gives an explanation of the results obtained.

Толық мәтін

Рұқсат жабық

Авторлар туралы

M. Mikhailov

Tomsk State University of Control Systems & Radioelectronics

Хат алмасуға жауапты Автор.
Email: membrana2010@mail.ru
Ресей, 634000, Tomsk

V. Goronchko

Tomsk State University of Control Systems & Radioelectronics

Email: W_Goronchko@mail.ru
Ресей, 634000, Tomsk

D. Fedosov

Tomsk State University of Control Systems & Radioelectronics

Email: Membrana2010@mail.ru
Ресей, 634000, Tomsk

A. Lapin

Tomsk State University of Control Systems & Radioelectronics

Email: Membrana2010@mail.ru
Ресей, 634000, Tomsk

S. Yuryev

Tomsk State University of Control Systems & Radioelectronics

Email: Membrana2010@mail.ru
Ресей, 634000, Tomsk

Әдебиет тізімі

  1. Vani P., Vinitha G., Sayyed M.I., Alshammari M.M., Manikandan N. // Nucl. Engineer. Technol. 2021. V. 53. Iss. 12. P. 4106. https://doi.org/10.1016/j.net.2021.06.009
  2. Marzouk M.A., Ghoneim N.A. // Radiation Phys. Chem. 2020. V. 174. P. 108893. https://doi.org/10.1016/j.radphyschem.2020.108893
  3. Chen J., Yu Y., Feng A., Mi L., Xiu H. // Ceram. Int. 2022. V. 48. Iss. 1. P. 754. https://doi.org/10.1016/j.ceramint.2021.09.155
  4. Kleiman J.I., Gudimenko Y., Iskanderova Z., Tennyson R.C., Morison W.D. Modification of Thermal Control Paints by PHOTOSIL™ Technology. // Protection of Space Materials from the Space Environment. Space Technology Proceedings, vol 4. / Eds. Kleiman J.I., Tennyson R.C. Dordrecht: Springer, 2001. P. 243. https://doi.org/10.1007/978-94-010-0714-6_19
  5. Mikhailov M.M., Vlasov V.A., Yuryev S.A., Neshchimenko V.V., Shcherbina V.V. // Dyes and Pigments. 2015. V. 123. P. 72. https://doi.org/10.1016/j.dyepig. 2015.07.024
  6. Bo Z., Gang L., Kangli C., Weimin C. Preparation and Space Environmental Stability of a Nano-Materials Modified Thermal Control Coating. // Protection of Space Materials from the Space Environment. Space Technology Proceedings, vol 47. / Ed. Kleiman J.I. Cham: Springer, 2017. P. 433. https://doi.org/10.1007/978-3-319-19309-0_43
  7. Михайлов М.М., Нещименко В.В., Скрипка Н.Г., Хохлов Р.Н. // Перспективные материалы. 2010. № 3. C.14.
  8. Dudin A.N., Iurina V.Yu., Neshchimenko V.V., Li C.L. // St. Petersburg Polytechnic University Journal – Phys. Math. 2022. V. 15. Iss. 3.1. P. 259. https://doi.org/10.18721/JPM.153.117
  9. Andrievskii R. // Rev. Adv. Mater. Sci. 2011. V. 29.
  10. Kositsyn L.G., Mikhailov M.M., Kuznetsov N.Y., Dvoretskii M.I. // Instrum. Experimental Tech. 1985. V. 28. P. 929.
  11. Artini C., Costa G.A., Pani M., Lausi A. // J. Solid State Chem. 2012. V. 190. P. 24. https://doi.org/10.1016/j.jssc.2012.01.056
  12. ASTM E490-00a. Standard Solar Constant and Zero Air Mass Solar Spectral Irradiance Tables, ASTM International, West Conshohocken, PA, 2019.
  13. Mikhailov M.M., Dvoretskii M.I. // Soviet Phys. J. 1988. V. 31. P. 591. https://doi.org/10.1007/BF00917556
  14. Kuznetsov V.N., Serpone N. // J. Phys. Chem. 2009. V. 113. № 34. P. 15110. https://doi.org/10.1021/jp901034t
  15. Blanco M., Coello J., Iturriaga H., Maspoch S., Pezue-la C. // Analyst 1998. V. 123. Iss. 8. P. 135. https://doi.org/10.1039/A802531B
  16. Blanco M., Villarroya I. // Trends in Analytical Chemistry. 2002. V. 21. Iss. 4. P. 240. https://doi.org/10.1016/S0165-9936(02)00404-1
  17. Trofimova E., Pustovarov V., Zatsepin A. // Physics of the Solid State. 2019. V. 61. P. 763. https://doi.org/10.1134/S1063783419050366
  18. ASTM E903 – 96. Standard Test Method for Solar Absorptance, Reflectance, and Transmittance of Materials Using Integrating Spheres, ASTM International, West Conshohocken, PA, 2012.
  19. Johnson F.S. // J. Meteorological. 1954. V. 11. № 5. P. 431. https://doi.org/10.1175/1520-0469(1954)011<0431: TSC>2.0.CO;2
  20. Новиков Л.С. // Радиационные воздействия на материалы космических аппаратов. М.: Унив. книга, 2010. С. 191.

Қосымша файлдар

Қосымша файлдар
Әрекет
1. JATS XML
Жүктеу
2. Fig. 1. Radiographs of powders: gd2o3 before (a) and after (b) electron irradiation, nGd2O3 before (c) and after (d) electron irradiation.

Жүктеу (274KB)
Метадеректер
3. Fig. 2. Diffuse reflection spectra of gd2o3 microdowder (1), nGd2O3 nanopowder (2) and solar radiation spectrum (3).

Жүктеу (135KB)
Метадеректер
4. Fig. 3. Granulometric composition of gd2o3 powder.

Жүктеу (75KB)
Метадеректер
5. Fig. 4. The edge of the main absorption of micro- and nanopowders Gd2O3.

Жүктеу (154KB)
Метадеректер
6. Fig. 5. Diffuse reflection spectra before (1) and after irradiation with electrons with an energy of 30 keV by fluence 1 (2), 2 (3), 3 × 1016 (4) cm–2 micro- (a) and nanopowders (b) Gd2O3.

Жүктеу (257KB)
Метадеректер
7. Fig. 6. Difference reflection spectra of micro-powder (a) and nanopowder (b) Gd2O3 after electron irradiation with fluence 1 (1), 2 (2), 3 × 1016 (3) See–2.

Жүктеу (244KB)
Метадеректер
8. Fig. 7. Dependence of the change in the absorption coefficient ∆as on the electron fluence for mGd2O3 (1) and Gd2O3 (2).

Жүктеу (95KB)
Метадеректер

© Russian Academy of Sciences, 2024